    題名: Phase separation of thin-film polymer mixtures under in-plane electric fields
    作者: Wang,CH;Chen,PL;Lu,CYD
    貢獻者: 物理學系
    關鍵詞: BLOCK-COPOLYMER MICROSTRUCTURE;SPINODAL DECOMPOSITION;POLY(METHYL METHACRYLATE);BLEND FILMS;POLYSTYRENE/POLY(METHYL METHACRYLATE);COLLOIDAL SUSPENSIONS;PS/PMMA BLEND;SURFACE;INTERFACE;MORPHOLOGY
    日期: 2010
    上傳時間: 2012-06-11 10:46:01 (UTC+8)
    出版者: 國立中央大學
    摘要: Phase-separation dynamics of polymer thin-film mixtures of polystyrene (PS) and poly(methyl methacrylate) (PMMA) are observed while an in-plane electric field is applied, instead of the out-of-plane fields usually employed previously. The phase separation is accompanied by the formation of PS dewetting holes at zero or weak fields. The dewetting velocity at 0.25 mu m/min is a few times slower than that seen in regular bilayer dewetting. With the increasing of the field strength, we observe the formation of PS droplets in PMMA matrix, a reversal from zero-or low-field conditions. The PS dewetting holes are also suppressed. At further increased fields, PS droplets quickly penetrate up to the top of the PMMA matrix, leading to smaller and more irregular final PS droplets. This is manifested in the dramatic decrease in the growth exponent of the droplet size L from L similar to t(1.5) to L similar to t(0.1). These morphology changes are explained by the electrostatic energy resulted from the PS and PMMA dielectric contrast.
    關聯: PHYSICAL REVIEW E
    顯示於類別:[物理學系] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML301檢視/開啟


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 隱私權政策聲明