奈米錫顆粒之超導與自旋極化間共存及互競現象; Coexistence and Competition between Superconductivity and Spin Polarization in Sn Nanoparticles.

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/7546

Title:	奈米錫顆粒之超導與自旋極化間共存及互競現象;Coexistence and Competition between Superconductivity and Spin Polarization in Sn Nanoparticles.
Authors:	陳姿蓉;Tzu-jung Chen
Contributors:	物理研究所
Keywords:	錫;超導;自旋極化;superconductivity;Sn;Tin;spin polarization
Date:	2008-06-20
Issue Date:	2009-09-22 10:59:44 (UTC+8)
Publisher:	國立中央大學圖書館
Abstract:	採用熱蒸鍍法製備錫奈米顆粒，以Sn_071205表示。透過AFM與X光繞射鑑定?徑為7 nm，從X光螢光分析與 X光繞射圖分析，確定Sn_071205樣品成份皆為錫，無氧化物或者其他元素。由磁化曲線及變溫磁化率曲線可觀察到Sn_071205樣品同時具有超導抗磁性及自旋極化效應，兩種效應可以共存。進一步以壓合的方式改變樣品顆?間距，在顆粒間距較大的區域，可觀察到超導抗磁性減弱且自旋極化增強，判斷兩種效應不單只有共存，彼此之間還會相互競爭。顆粒間距S=9.5 nm時，庖立順磁磁化率與飽和磁化強度同時具有極大值。於顆粒間距S=6.9 nm時，樣品產生轉變，庖立順磁磁化率與飽和磁化強度同時逆勢變小，且於實驗溫度1.8 K以上觀察不到超導抗磁性，之後繼續壓合超導抗磁性又逐漸增強。探討超導臨界溫度隨顆粒間距變化趨勢，受到超導能隙Δ以及平均單電子能階分離能隙δ隨顆粒間距變化的影響，其關係曲線共可區分為四個區域。此外在低聚合密度的區間，超導抗磁性的減弱使得穿透深度隨顆粒間距縮短而逐漸加深，與本實驗室去年的研究大致上相符合。 Sn nanoparticles were fabricated by thermal evaporation method. Atomic force microscope images and x-ray diffraction patterns were performed to examine particle diameter and composition. A pure 7 nm Sn nanoparticle powder was obtained. No trace of oxidation or other impurity was found. AC magnetic susceptibility and magnetization measurements were performed to study the magnetic properties. Superconductivity and spin polarization were observed to coexist at low temperatures. To study the interplay between spin polarization and superconductivity, the M-H curves at different interparticle separations were measured. Coexistence and competition between superconductivity and spin polarization were found for inter-particle separation that is greater than 6.9 nm. No superconductivity may be found at an inter-particle separation of 6.9 nm. As the inter-particle separation was reduced further, the superconductivity signals recovered. The inter-particle interactions linked to the critical temperature can be divided into four regimes. It is the competition between superconductivity and spin polarization that govern the behavior.