實驗室內評估發泡用水含量於溫拌發泡瀝青混凝土性能之影響;The Performance of Foamed Warm Mix Asphalt with Various Foaming Water Content

NCUIR > Engineering College > Graduate Institute of Civil Engineering > Electronic Thesis & Dissertation > Item 987654321/94509

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/94509

Title:	實驗室內評估發泡用水含量於溫拌發泡瀝青混凝土性能之影響;The Performance of Foamed Warm Mix Asphalt with Various Foaming Water Content
Authors:	邱俊穎;CHUN-YING, CHIU
Contributors:	土木工程學系
Keywords:	溫拌瀝青混凝土;發泡水量;水分侵害;水泥;Warm Mix Asphalt;Foaming Water Content;Moisture Damage;Cement
Date:	2024-07-30
Issue Date:	2024-10-09 14:50:26 (UTC+8)
Publisher:	國立中央大學
Abstract:	溫拌技術相較於熱拌具有降低能源消耗和碳排放的優勢，且經國外多年應用發展已相當成熟，國內亦具備生產溫拌瀝青混凝土的能力，勢必成為道路工程的重要趨勢。然而相關研究指出溫拌瀝青混凝土雖然於現地之車轍與水分侵害情形與熱拌瀝青混凝土無異，但試驗室內評估其浸水殘餘強度可能無法通過規範，以致無法使用，且發泡水量對溫拌發泡瀝青混凝土的影響程度尚不明確，故須以研究探討適當配置。本研究欲探討發泡水量對溫拌發泡瀝青混凝土之影響以及與熱拌瀝青混凝土之差異，並探討不同填充料對瀝青混凝土之性能影響，首先以不同發泡水量的溫拌發泡瀝青混凝土進行間接張力試驗、浸水殘餘強度試驗、漢堡輪跡試驗、Ideal Rutting Test與Indirect Tensile Cracking Test等成效試驗後與熱拌進行比較，再將填充料由石粉替換為水泥進行成效比較，試驗結果顯示不同發泡水量之溫拌發泡瀝青混凝土之包裹性及壓實能力皆可符合需求，且成效在統計上無顯著差異。然而溫拌與熱拌比較結果僅1%水量之成效試驗相比均無顯著差異。在填充料的比較中水泥相較於石粉可明顯提升溫拌發泡瀝青混凝土的浸水殘餘強度，故作為溫拌發泡瀝青混凝土的填充料更為合適。;Compared to hot mix, warm mix technology offers the advantages of reducing energy consumption and carbon emissions. The application of warm mix technology has been developed abroad for years. Domestically, the capability to produce warm mix asphalt concrete is also in place, making it certain to become an important trend in pavement engineering. According to related research, although the rutting and moisture damage of warm-mix asphalt concrete (WMA) in the field is similar to the hot-mix asphalt concrete (HMA). The Tensile Strength Ratio of WMA evaluated in the laboratory may not meet specifications, causing it unusable. Therefore, it is necessary to investigate the appropriate configurations for WMA. Furthermore, the impact of foaming water content on foamed warm mix asphalt concrete (FWMA) remains unclear, necessitating further research to determine the appropriate mix design. This study aims to examine the effect of foaming water on FWMA and its differences from HMA, as well as the impact of various fillers on asphalt concrete performance. Initially, FWMA samples with different foaming water contents were subjected to several performance tests, including the Indirect Tensile Test, Tensile Strength Ratio, Hamburg Wheel Tracking Test, Ideal Rutting Test, and Indirect Tensile Cracking Test, and the results were compared with HMA samples. Subsequently, the filler material was switched from limestone to cement for further comparison. The test results indicated that WMA with different foaming water contents met the requirements for coating and compactability, with no statistical significance in performance. However, when comparing the performance of only 1% foaming water, no statistical significance were observed between FWMA and HMA. In the comparison of using different fillers, cement significantly improved the Tensile Strength Ratio of FWMA over limestone, making it a more suitable filler material.
Appears in Collections:	[Graduate Institute of Civil Engineering] Electronic Thesis & Dissertation

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	13	View/Open

社群 sharing

Loading...