摘要： This paper reports on a hydrogen storage material of poly(methyl acrylate) and methylamine borane (PMA/MeAB) composite, which is synthesized by a simple solution-blending process at room temperature. The thermal decomposition process of the as-prepared composite is investigated by temperature programmed desorption/mass spectrometer (TPD/MS), thermogravimetry (TG) measurements and water displacement method. It is found that PMA/MeAB100 (100 mg PMA with 100 mg MeAB) starts to release H2 at the temperature of 90.5 °C with the dehydrogenation peak centered at 120.7 °C. This is about 20 °C lower than that of neat MeAB. Meanwhile, the evaporation of MeAB and the volatile byproducts from the dehydrogenation stage of PMA/MeAB100 are also suppressed. The present result shows that the dehydrogenation property of MeAB is enhanced by using PMA/MeAB composite. ► A hydrogen storage material of poly(methyl acrylate) and methylamine borane (PMA/MeAB) composite has been synthesized at room temperature. ► The PMA/MeAB composite starts to release H2 at the temperature of 90.5 °C, which is much lower than that of neat MeAB. ► The PMA/MeAB composite shows an enhancement of the dehydrogenation kinetic and the suppression of the releasing byproducts. 出版者： Kidlington: Elsevier Ltd 出版日期： 2012-05-01 出處： International journal of hydrogen energy, 2012-05, Vol.37 (9), p.7638-7644 資源來源： Elsevier ScienceDirect Journals Complete 版權： 2012 Hydrogen Energy Publications, LLC. 版權： 2014 INIST-CNRS 識別號： ISSN: 0360-3199 識別號： EISSN: 1879-3487 識別號： DOI: 10.1016/j.ijhydene.2012.01.134 識別號： CODEN: IJHEDX