Title:	Discuss the effective electrode distance of accelerated Lithium Migration Technique from the viewpoint of ion migration
Authors:	王韡蒨;Wang), 王韡蒨(Wei-Chien;Lee), 李釗(Chau;Liu), 劉志堅(Chih-Chien;Tsai), 蔡欣妤(Hsin-Yu;Yu), 游雁斐(Yen-Fei
Contributors:	工學院土木工程學系
Keywords:	Accelerated Lithium Migration Technique;alkali–silica reaction;concrete;EI;electrode distance;Scopus;加速鋰離子傳輸技術;混凝土;電極間距;鹼-矽反應
Date:	2014-01-01
Issue Date:	2026-04-21 13:40:12 (UTC+8)
Publisher:	Chinese Institute of Civil and Hydraulic Engineering;台灣: 中國土木水利工程學會
Abstract:	摘要：加速鋰離子傳輸技術（ALMT）是發展用於抑制混凝土的鹼-矽反應（ASR）問題，當施加定電壓時，離子傳輸的速率會受到混凝土結構及電極間距影響，本研究對三種不同水灰比混凝土施加60V定電壓，使用不同試體長度以調整電極間距分別為8、16、24、32及38cm，進行ALMT試驗，過程中監測陰極電解液內的鋰、鈉及鉀離子濃度，通電結束時間以鹼質不再明顯移出或電流密度降到1A/m^2加以決定，藉建立離子濃度與累積電荷量關係，評估離子傳輸效能，以分析電極間距對ALMT離子傳輸的影響。試驗結果顯示，混凝土水灰比愈大，愈有利於離子傳輸。初始電流會隨電極間距增加而降低，離子傳輸效能減少。當水灰比為0.48、0.58及0.68時，電極間距分別在16、24及32cm以下，有較佳的離子傳輸效能，且可移出混凝土所含含鹼量達80%以上，送入足夠的鋰離子，因此，針對不同水灰比，上述電極間距可作為ALMT實務應用時的有效上限。出版者：台灣: 中國土木水利工程學會出版日期： 2014-09-01 出處：中國土木水利工程學刊, 2014-09, Vol.26 (3), p.229-234 資源來源：華藝CEPS中文電子期刊服務識別號： ISSN: 1015-5856 識別號： DOI: 10.6652/JoCICHE.201409_26(3).0007