中大機構典藏-NCU Institutional Repository-提供博碩士論文、考古題、期刊論文、研究計畫等下載:Item 987654321/39011
English  |  正體中文  |  简体中文  |  Items with full text/Total items : 81570/81570 (100%)
Visitors : 47011773      Online Users : 122
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/39011


    Title: High-transparency Ni/Au ohmic contact to p-type GaN
    Authors: Sheu,JK;Su,YK;Chi,GC;Koh,PL;Jou,MJ;Chang,CM;Liu,CC;Hung,WC
    Contributors: 物理研究所
    Keywords: INDIUM TIN OXIDE;FIELD-EFFECT TRANSISTORS;N-GAN;RESISTANCE
    Date: 1999
    Issue Date: 2010-07-08 14:02:07 (UTC+8)
    Publisher: 中央大學
    Abstract: In this study, a very thin Ni/Au bilayer metal film was prepared by electron beam evaporation and thermal alloying to form ohmic contact on p-type GaN film. After thermal alloying, the current-voltage (I-V) characteristic of Ni/Au contact on p-type GaN film exhibited ohmic behavior. The Ni/Au contacts showed a specific contact resistance of 1.7 x 10-(2) Ohm cm(2) at an alloying temperature of 450 degrees C. In addition, the light transmittance of the Ni/Au (2 nm/6 nm) bilayer on p-type GaN was measured to be around 85% at 470 nm. These results suggest that a suitable metallization technology for the fabrication of light emitting devices can be achieved. (C) 1999 American Institute of Physics. [S0003-6951(99)00816-5].
    Relation: APPLIED PHYSICS LETTERS
    Appears in Collections:[Graduate Institute of Physics] journal & Dissertation

    Files in This Item:

    File Description SizeFormat
    index.html0KbHTML573View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 隱私權政策聲明