Pyrolytic carbons from acid/base-treated rice husk as lithium-insertion anode materials

NCU Institutional Repository > 工學院 > 化學工程與材料工程學系 > 期刊論文 > Item 987654321/49895

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/49895

题名:	Pyrolytic carbons from acid/base-treated rice husk as lithium-insertion anode materials
作者:	Fey,GTK;Cho,YD;Chen,CL;Lin,YY;Kumar,TP;Chan,SH
贡献者:	化學工程與材料工程學系
关键词:	LI-ION BATTERIES;CAPACITY DISORDERED CARBONS;CARBONACEOUS MATERIALS;MICROPOROUS CARBONS;ACTIVATED CARBONS;LARGE HYSTERESIS;SUGAR CARBONS;HARD CARBONS;MECHANISM;INTERCALATION
日期:	2010
上传时间:	2012-03-27 16:25:49 (UTC+8)
出版者:	國立中央大學
摘要:	The effects of hydrochloric acid and sodium hydroxide as leachants on the lithium-insertion properties of pyrolytic carbons prepared from rice husk are presented. All the disordered carbonaceous products had interlayer spacings (d(002)) of more than 3.7 angstrom, with values decreasing with an increase in the concentration of the leachant. The values of the H/C ratio and the R-parameter, the reciprocal of which is a measure of the number of non-parallel single layers of carbon, also diminished with an increase in the concentration of NaOH. An increase in the alkali concentration was found to improve the porosity of the carbons, as evidenced by the Brunauer-Emmett-Teller (BET) surface area data. An interaction of these factors determines the observed capacities of the carbon products. The highest insertion and deinsertion capacities were observed with the carbon obtained from rice husk treated with 0.3 M NaOH, the values being 819 and 463 mAh/g, respectively.