Effects of Mg Content on Microstructure and Mechanical Properties of Al-14.5Si-4.5Cu Alloy

NCUIR > Engineering College > Departmant of Mechanical Engineering > journal & Dissertation > Item 987654321/50068

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/50068

Title:	Effects of Mg Content on Microstructure and Mechanical Properties of Al-14.5Si-4.5Cu Alloy
Authors:	Wu,CT;Lee,SL;Hsieh,MH;Lin,JC
Contributors:	機械工程學系
Date:	2010
Issue Date:	2012-03-27 17:02:45 (UTC+8)
Publisher:	國立中央大學
Abstract:	This study elucidates how Mg content affects the microstructure and mechanical properties of Al-14.5Si-4.5Cu alloy by adding 0.45 and 0.90 wt pct Mg. Primary silicon, eutectic silicon, acicular beta-Al(5)FeSi, Al(2)Cu, and Al(5)Cu(2)Mg(8)Si(6) phases were observed under the as-cast condition in low-Mg alloy. In high-Mg alloy, a large proportion of the acicular beta-Al(5)FeSi phase was converted to Chinese script Al(8)Mg(3)FeSi(6) phase. Neither the acicular beta-Al(5)FeSi phase nor the Chinese script Al(8)Mg(3)FeSi(6) phase dissolved in the Al matrix during solution heat treatment. Tensile testing indicates that T6-treated high-Mg alloy containing the Chinese script Al(8)Mg(3)FeSi(6) phase is better than the T6-treated low-Mg alloy that contains the acicular beta-Al(5)FeSi phase. The morphologies of Chinese script Al(8)Mg(3)FeSi(6) and acicular beta-Al(5)FeSi phases affect the tensile properties of Mg-containing Al-14.5Si-4.5Cu alloys. Additionally, high-Mg alloy contains a higher concentration of Mg solute atoms in the Al matrix than low-Mg alloy, and so the former contains more lambda' precipitates (Al(5)Cu(2)Mg(8)Si(6)) after T6-tempering treatment. The large amount of lambda' that precipitates in T6-treated high-Mg alloy may also enhance its tensile strength. The ultimate tensile strength (UTS) and elongation of the high-Mg alloy are superior to those of the low-Mg alloy.
Relation:	METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
Appears in Collections:	[Departmant of Mechanical Engineering ] journal & Dissertation