高壓系統下親/疏水性吸附劑之吸附行為與再生能耗探討;none

NCUIR > Engineering College > National Central University Department of Chemical & Materials Engineering > Electronic Thesis & Dissertation > Item 987654321/53725

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/53725

Title:	高壓系統下親/疏水性吸附劑之吸附行為與再生能耗探討;none
Authors:	陳冠銘;Chen,Kuan-ming
Contributors:	化學工程與材料工程研究所
Keywords:	水汽吸附;變溫吸附;吸附乾燥機;none
Date:	2012-07-24
Issue Date:	2012-09-11 18:12:18 (UTC+8)
Publisher:	國立中央大學
Abstract:	壓縮乾燥空氣係經空氣壓縮機與穩壓儲存桶降溫後，先經冷凍乾燥設備除濕，再以無熱式或加熱式雙塔吸附乾燥設備將高壓空氣乾燥至壓力露點溫度-40℃或-70℃。為了尋找具節能且適用於壓縮空氣吸附乾燥設備之吸附劑，本研究於高壓系統狀態下，探討不同吸附劑表面特性對吸附/脫附現象之影響與再生能耗分析。其中4A、13X、Al2O3、ZSM-5-260、ZSM-5-38作為主要吸附劑應用於壓縮空氣系統之乾燥設備中，並進行減少能耗的脫附方法研究，以找到最適當之吸附劑以及吸附條件。並尋找最佳能耗的條件並符合高壓空氣使用之需求，以利將來應用於雙塔式加熱再生乾燥設備中。故本研究成果可提供壓縮空氣乾燥設備選取吸附劑時之節能參考。實驗結果顯示在高壓系統下活性氧化鋁有最低之能耗。Compressed air is usually produced by air compressor, cooled down with the pressure-stabilized storage barrels and primarily dehumidified via refrigeration dryer. And then a heatless or heat-driven dual-bed adsorption dryer futhermore reduces moisture to reach dew point temperature of -40℃ or -70 ℃. In order to develop a high-efficiency energy-saving adsorbent in adsorption dryer, this study was to investigate the adsorption and desorption behavior and regeneration energy consumption affected by adsorbents characteristic at high pressure status. The adsorbents of 4A, 13X, ZSM-5-260, Al2O3 and ZSM-5-38 were measured in the study to find the lowest energy consumption and optimal desorption method. The results could be applied to screen the optimum adsorbents for high-efficiency thermal-regeneration adsorption dryer in compressed air system. In this research, experement results show that the adsorbent of the lowest regeneration energy consumption under high pressure system is activated alumina.
Appears in Collections:	[National Central University Department of Chemical & Materials Engineering] Electronic Thesis & Dissertation

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	808	View/Open

社群 sharing

Loading...