以(100)矽基板上的氮化硼研製P型異質場效電晶體;Fabrication of P-Channel Heterostructure Field Effect Transistors with the Boron Nitride Grown on Si(100) Substrates

NCU Institutional Repository > 理學院 > 光電科學研究所 > 博碩士論文 > Item 987654321/97679

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://ir.lib.ncu.edu.tw/handle/987654321/97679

题名:	以(100)矽基板上的氮化硼研製P型異質場效電晶體;Fabrication of P-Channel Heterostructure Field Effect Transistors with the Boron Nitride Grown on Si(100) Substrates
作者:	蔣以約;Chiang, Yi-Yue
贡献者:	光電科學與工程學系
关键词:	高電子遷移率電晶體;遷移率;電晶體;二維電洞氣;霍爾量測;HFET;HEMT;p-channel;2DHG;hall measurement
日期:	2025-07-25
上传时间:	2025-10-17 11:46:36 (UTC+8)
出版者:	國立中央大學
摘要:	本論文探討氮化硼（boron nitride, BN）成長於矽（Si）基板上的異質結構特性，並嘗試以此磊晶結構所形成的二維電洞氣（two-dimensional hole gas, 2DHG），研製P型異質場效電晶體。在實驗部分，我們使用金屬有機化學氣相沉積法（metal-organic chemical vapor deposition, MOCVD）於 Si(100) 基板上成長 BN 薄膜，形成BN/Si 異質結構。藉由低溫霍爾量測，我們發現BN/Si介面在 13 K 至 300 K 溫度範圍內，有極高的電洞濃度，穩定維持在 1.7~2.0 × 1015 cm−2，遷移率則介於 48~54 cm2/V⋅s，不會隨著溫度改變，呈現明顯的2DHG特性，與常見的摻雜(acceptor-doped)電洞不同。為驗證此結構於元件上的應用潛力，我們製作具閘極控制之 P-channel 高電子遷移率電晶體（Heterostructure Field Effect Transistors, HFET），並進行直流電性量測。元件展現常開（depletion-mode）特性，且具備初步的閘極調變能力，顯示出 BN on Si 結構具備場效應控制特性，有機會應用在寬能隙 CMOS 邏輯電路。 ;This study aims to fabricate a p-channel heterostructure field effect transistor (HFET) with the boron nitride (BN) grown on Si(100) substrates. The BN layer was deposited on a Si (100) substrate using metal-organic chemical vapor deposition (MOCVD). According to the results of low-temperature Hall measurements (13K ~ 300K), the BN/Si interface delivered a stable hole density at 1.7~2.0 × 1015 cm−2, and hole mobility at 48~54 cm2/V⋅s, showing the two-dimensional hole gas (2DHG) behavior. The result is not attainable with the holes by acceptor doping, which exhibiting strong temperature dependence. To explore the possibility in device applications, the BN-based p-channel HFETs were fabricated and characterized by DC measurements. The device exhibited the depletion-mode characteristics and demonstrated limited gate modulation capability. The result indicates that the 2DHG at BN/Si can be controlled by gate voltage, showing a potential for wide-bandgap CMOS logic circuits.