摘要(英) |
The copper nanoparticles were manufactured by the thermal evaporation method. We got the sample of cuprous oxide from a process that heated the copper in a condition in which not enough oxygen, and got the sample of cupric oxide from the process that heated in air. The chemical composition of the sample were pure Cu2O and CuO by X-ray diffraction and General Structure Analysis System. The mean particle diameter of Cu2O and CuO nanoparticles were 5.5 nm and 3.6 nm that determined respectively by X-ray diffraction patterns.
Magnetic properties of nanoparticles were measured by Physical Property Measurement System. The M(H) of Cu2O in various temperature were observed, then fitted the M(H) curve by a Langevin function, a Brillouin function and a diamagnetic term. From a result of fitting curve at all temperature, there were three effect in the system, spin polarization, Zeeman effect, diamagnetic term. At low temperature, the M(H) of Cu2O could be represented by spin polarization and Zeeman effect, then at high temperature, M(H) could be predominated by spin polarization and diamagnetic term. Looking the M(H) curve of CuO, it showed there were two components in the system at low temperature, spin polarization and Zeeman effect. M(H) was risen with magnetic field increasing at high temperature, there was other term in the system. By fitting Ms(T) and M(T),we observed that it had spin wave in the nanoparticle system. By the XRD patterns, we observed that Cu2O had a property of the negative thermal expansion at 150~180 K, and it had a relation with charge density transition.
|
參考文獻 |
第一章
[1] 銅氧核殼奈米顆粒間交互作用對自旋極化之影響, 陳乃維, 國立中央大學碩士論文(2008)
[2] J. M. Zuo, M. Kim, M. O'Keeffe and J. C. H. Spence, NATURE 401
(1999)
[3] 奈米科技高逢時 科學發展 2005年2月386期
[4] H. Hori, T. Teranishi, Y. Nakae, Y. Seino, M. Miyake, and S. Yamada, Phys. Lett. A 263, 406 (1999).
[5] B. Sampedro, P. Crespo, A. Hernando, R. Litrán, J. C. Sánchez López, C. LópezCartes, A. Fernandez, J. Ramírez, J. González Calbet, and M. Vallet,Phys. Rev. Lett. 91, 237203 (2003).
[6] V. Kumar and Y. Kawazoe, Eur. Phys. J. D 24, 81 (2003).
[7] Y. Yamamoto, T. Miura, M. Suzuki, N. Kawamura, H. Miyagawa, T. Nakamura,K. Kobayashi, T. Teranishi, and H. Hori, Phys. Rev. Lett. 93, 116801 (2004).
[8] 顆粒間交互作用對奈米金自發性磁性之影響,郭彥廷,國立中央大學碩士論文(2008)
第二章
[1] 材料分析,汪建民中國材料學學會(2008)
[2] 氧化亞銅奈米顆粒的熱縮現象探討吳政道 國立中央大學碩士論文(2009)
[3] 銅與氧化銅奈米微粒之自旋極化效應沈奕廷 國立中央大學說是論文(2011)
[4] X光繞射原理與材料結構分析許樹恩、吳泰伯中國材料學學會(2006)
[5] 擬合X光繞射峰形判定奈米微粒粉末的粒徑分佈王進威 國立中央大學碩士論文(2006)
第三章
[1] 材料分析,汪建民中國材料學學會(2008)
[2] 氧化亞銅奈米顆粒的熱縮現象探討吳政道 國立中央大學碩士論文(2009)
[3] 銅與氧化銅奈米微粒之自旋極化效應沈奕廷 國立中央大學說是論文(2011)
[4] X光繞射原理與材料結構分析許樹恩、吳泰伯中國材料學學會(2006)
[5] 擬合X光繞射峰形判定奈米微粒粉末的粒徑分佈王進威 國立中央大學碩士論文(2006)
第四章
[1] W. Schäfer, A. Kirfel, A. Kirfel Appl. Phys. A 74 [Suppl.], S1010–S1012 (2002)
[2] 氧化亞銅微粒的自發性自組奈米線之研究紀忠義 國立東華大學碩士論文(2009)
|