摘要(英) |
In the communications field, the need for high-speed transport and large-bandwidth data communication is increasing rapidly. Comparing to the copper conductor in electrical communication, the optical waveguide provides higher speed, wider bandwidth, and lower loss. Thus, the application of silicon photonics become a good candidate for the next generation communication. The basic operation system includes photonics circuit for communication and electronics circuit for computation. The electrical signal is converted into optical signal by modulating either the intensity or the phase of a laser. Then, the optical signal is transported by the optical fiber externally and the optical waveguide internally. For the receiver, the optical signal is converted back into electrical signal by an optical receiver. Besides, for high-power optical sources, there are significant applications in various domains including optical amplifiers, Raman lasers, medicine, and spectroscopy. Recently, these studies have been investigated in on-chip systems, especially for generating optical nonlinear signals.
To study optical nonlinearity, high optical power is a must. However, during the measurement of optical fibers coupling to waveguides with high input power, the mechanical vibration of the optical fiber would be a critical problem for coupling stability. Traditionally, it can be compromised by fabricating either V- or U-Groove structures. U-Groove was first made in the off-chip type. As the demands for photonics increase, U-Groove is gradually developed into the on-chip type. In the past, these on-chip U-Grooves are widely used and patterned after the waveguide formation. In this thesis, we present a new fabrication process, Groove-first, which U-Grooves were formed before the waveguide formation. Groove-first process can solve the problem of silicon nitride film stress by combining the strain-relaxed pattern during U-Groove formation. Also, this process can prevent the etching of silicon oxide and mass produce U-Groove chips. In terms of waveguide, unwanted process onto the waveguide structure can be avoided. The natural inverse taper waveguide can be formed by MA6 which break its resolution limit.
In the first part of this thesis, we will discuss the fabrication and process optimization of U-grooves before patterning the waveguide. Second, silicon nitride-based waveguides were chosen to be the photonic platform for fiber-waveguide interconnection. Last, we will show that the measurement error caused by the mechanical vibration could be released comparing to the traditional coupling without the grooves and the power variation is found to be below 10% even with the input power up to 800mW. |
參考文獻 |
[1] Tsao, Shyh-Lin, Huang-Chen Guo, and Chun-Wei Tsai. "A novel 1× 2 single-mode 1300/1550 nm wavelength division multiplexer with output facet-tilted MMI waveguide." Optics Communications 232.1-6 (2004): 371-379.
[2] Baets, Roel, et al. "Silicon Photonics: silicon nitride versus silicon-on-insulator." Optical Fiber Communication Conference. Optical Society of America, 2016.
[3] Hideur, Ammar, et al. "Dynamics and stabilization of a high power side-pumped Yb-doped double-clad fiber laser." Optics Communications 186.4-6 (2000): 311-317.
[4] Karpov, V. I., et al. "Laser-diode-pumped phosphosilicate-fiber Raman laser with an output power of 1 W at 1.48 µm." Optics letters 24.13 (1999): 887-889.
[5] Bashkansky, Mark, et al. "Characteristics of a Yb-doped superfluorescent fiber source for use in optical coherence tomography." Optics Express 3.8 (1998): 305-310.
[6] Chernikov, S. V., et al. "1083 nm ytterbium doped fibre amplifier for optical pumping of helium." Electronics letters 33.9 (1997): 787-789.
[7] Goldberg, Lew, et al. "High-power superfluorescent source with a side-pumped Yb-doped double-cladding fiber." Optics letters 23.13 (1998): 1037-1039.
[8] Moss, David J., et al. "New CMOS-compatible platforms based on silicon nitride and Hydex for nonlinear optics." Nature photonics 7.8 (2013): 597-607.
[9] Den Hartog, Jacob Pieter. Mechanical vibrations. Courier Corporation, 1985.
[10] Ehsan, Abang Annuar, Sahbudin Shaari, and Mohd Kamil Abd Rahman. "Machining of acrylic-based Y-branch plastic optical fiber coupler with suspended waveguide taper." Optical review 19.1 (2012): 7-12.
[11] Kremmel, Johannes, et al. "Passively aligned multichannel fiber-pigtailing of planar integrated optical waveguides." Optical Engineering 56.2 (2017): 026115.
[12] Galan, J. V., et al. "CMOS compatible silicon etched V-grooves integrated with a SOI fiber coupling technique for enhancing fiber-to-chip alignment." 2009 6th IEEE International Conference on Group IV Photonics. IEEE, 2009.
[13] Ferdous, Fahmida, et al. "Spectral line-by-line pulse shaping of on-chip microresonator frequency combs." Nature Photonics 5.12 (2011): 770-776.
[14] Jiang, Yang, et al. "Recent progress of GaN growth on maskless chemical-etched grooved sapphire substrate." Energy & Environmental Science 4.8 (2011): 2625-2629.
[15] Kodama, Masahito, et al. "GaN-based trench gate metal oxide semiconductor field-effect transistor fabricated with novel wet etching." Applied physics express 1.2 (2008): 021104.
[16] Krause, P., and E. Obermeier. "Etch rate and surface roughness of deep narrow U-grooves in (110)-oriented silicon." Journal of Micromechanics and Microengineering 5.2 (1995): 112.
[17] Bean, Kenneth E. "Anisotropic etching of silicon." IEEE Transactions on electron devices 25.10 (1978): 1185-1193.
[18] Shikida, Mitsuhiro, et al. "A model explaining mask-corner undercut phenomena in anisotropic silicon etching: a saddle point in the etching-rate diagram." Sensors and Actuators A: Physical 97 (2002): 758-763.
[19] Boufnichel, Mohamed, et al. "Origin, control and elimination of undercut in silicon deep plasma etching in the cryogenic process." Microelectronic Engineering 77.3-4 (2005): 327-336.
[20] Lin, Nathan C., et al. "Visible-range silicon nitride edge coupler with U-groove passive alignment." 2020 Opto-Electronics and Communications Conference (OECC). IEEE, 2020.
[21] Xuan, Yi, et al. "High-Q silicon nitride microresonators exhibiting low-power frequency comb initiation." Optica 3.11 (2016): 1171-1180.
[22] Park, Suntak, Jong-Moo Lee, and Sang Choon Ko. "Fabrication method for passive alignment in polymer PLCs with U-grooves." IEEE photonics technology letters 17.7 (2005): 1444-1446.
[23] Joshi, B. C., et al. "LPCVD and PECVD silicon nitride for microelectronics technology." (2000).
[24] Tai, Y. C., and R. S. Muller. "Fracture strain of LPCVD polysilicon." (1988): 88-91.
[25] Scott, Gregory, et al. "NMOS drive current reduction caused by transistor layout and trench isolation induced stress." International Electron Devices Meeting 1999. Technical Digest (Cat. No. 99CH36318). IEEE, 1999.
[26] Ren, Guanghui, et al. "Study on inverse taper based mode transformer for low loss coupling between silicon wire waveguide and lensed fiber." Optics Communications 284.19 (2011): 4782-4788.
[27] Minhas, Ashudeep, et al. "AZ4620 Photoresist as an Alternative Sacrificial Layer for Surface Micromachining." Journal of Electronic Materials 49.12 (2020): 7598-7602.
[28] Adam, Tijjani, and U. Hashim. "The effect of exposure time and development time on photoresist thin film in Micro/Nano structure formation." 2012 10th IEEE International Conference on Semiconductor Electronics (ICSE). IEEE, 2012.
[29] Gogolides, E., et al. "Thermal and mechanical analysis of photoresist and silylated photoresist films: Application to AZ 5214™." Microelectronic engineering 30.1-4 (1996): 267-270.
[30] Andok, Robert, et al. "THE AZ 5214E RESIST IN EBDW LITHOGRAPHY AND ITS USE AS A RIE ETCH–MASK IN ETCHING THIN AG LAYERS IN N2 PLASMA." Journal of Electrical Engineering 64.6 (2013): 371-375. |