姓名	葉唐喬(Tang-Chiao Yeh)  查詢紙本館藏	畢業系所	物理學系
論文名稱	在環境條件下用膠帶劈裂Bi2Te3晶體的表面改質研究 (The Study of The Surface Modification of Bi2Te3 Crystals Cleaved with Tapes under Ambient Conditions)
相關論文	★ Exploration of new methods for growing Ag films on Au(111) studied by ARPES ★ 二階段成長法成長銀薄膜在銅(111)面上利用光電子能譜研究 ★ 利用角解析光電子能譜術研究銅薄膜在銀(111)基板上的成長 ★ 利用角解析光電子能譜術探測Ag/Au(111)系統中銀表面態受到光誘發的衰變情形 ★ 利用角解析光電子能譜術探測Ag/Au(111)系統中銀表面態受到光誘發的衰變情形 ★ Sulfur adsorption on Au(100): XPS, LEED and STM study ★ Adsorption and desorption of atomic hydrogen on the surface of thin Ag films on Au(111) studied with ARPES and XPS ★ Thin-film growth of Bi and S on Au(100) studied with LEED and XPS ★ Silicon adsorption on Ag(111): XPS and LEED study ★ The growth of Bi on Ag(111) studied with STM, LEED and XPS ★ The investigation of highly ordered Ag films on mica with STM, LEED and XPS ★ 原子級平整SrTiO3(100)表面製備過程中之表面重構、表面形貌以及表面元素組成之變化 ★ 使用熱處理生長單晶銅箔 ★ 碲與銻在銀(111)/白雲母表面的成長
檔案	[Endnote RIS 格式]    [Bibtex 格式]    [相關文章]   [文章引用]   [完整記錄]   [館藏目錄]   [檢視]  [下載] 本電子論文使用權限為同意立即開放。 已達開放權限電子全文僅授權使用者為學術研究之目的，進行個人非營利性質之檢索、閱讀、列印。 請遵守中華民國著作權法之相關規定，切勿任意重製、散佈、改作、轉貼、播送，以免觸法。
摘要(中)	在本研究中，我們使用膠帶劈裂以熔融法成長 Bi2Te3 晶體。透過低能量電子 繞射儀(Low Energy Electron Diffraction, LEED)、X 光光電子能譜術(X-ray Photoelectron Spectroscopy, XPS) 及 掃 描 穿 隧 顯 微 鏡 (Scanning Tunneling Microscope, STM)檢測 Bi2Te3 晶體在大氣、真空、氮氣及氧氣四種環境中劈裂的 表面改質現象。在真空環境中劈裂的 Bi2Te3 表面額外透過角解析光電子能譜術 (Angle-Resolved Photoelectron Spectroscopy, ARPES)檢測其能帶結構。在大氣環境 中劈裂的 Bi2Te3 表面一開始會受水氣侵蝕而產生 Bi 雙層，持續暴露則受到明顯 的氧化。在真空環境下劈裂的 Bi2Te3 表面並無觀察到任何改質現象，費米能階附 近呈現明顯的表面色散關係，顯示晶體表面仍維持高度有序且雜質與缺陷濃度低。因此在真空中以膠帶簡單劈裂Bi2Te3 的操作方式仍可維持樣品品質。在一大氣壓 的氮氣或氧氣背景中劈裂的表面會受到膠帶中汙染物的影響，存在些微水氣及碳 汙染，但未觀察到氧化現象。Bi2Te3 表面受到水氣侵蝕後可觀察到 Bi 雙層的 Bi4f 譜線及三重對稱的表面凹坑。表面進一步氧化後，有序結構受到破壞，並且無法 透過加熱恢復。
摘要(英)	In this study, we grew Bi2Te3 crystals using the melt-growth method and cleaved the surfaces of samples using tape. The surface modifications of the cleaved Bi2Te3 crystals were investigated in four different environments: atmospheric, vacuum, nitrogen, and oxygen, using Low Energy Electron Diffraction (LEED), X-ray Photoelectron Spectroscopy (XPS), and Scanning Tunneling Microscopy (STM). The Bi2Te3 samples cleaved in the vacuum environment were additionally characterized using Angle-Resolved Photoelectron Spectroscopy (ARPES) to examine their band structure. In the atmospheric environment, the cleaved Bi2Te3 surfaces initially experienced moisture erosion, leading to the formation of a Bi bilayer, which further underwent noticeable oxidation upon prolonged exposure. No surface modifications were observed on the Bi2Te3 surfaces cleaved in the vacuum environment, and the presence of a well-defined surface dispersion relation near the Fermi level indicated a highly ordered surface with low impurity and defect densities. Thus, the method of tape cleaving in vacuum could still maintain the sample quality. However, surfaces cleaved in 1atm of nitrogen or oxygen atmosphere were influenced by contaminants present in the tape, resulting in slight moisture and carbon contamination, while no oxidation was observed. After moisture erosion on the Bi2Te3 surface, Bi bilayer features in the Bi4f spectra of Bi2Te3 and some symmetric surface pits were observed. Further oxidation of the surface led to the destruction of the ordered structure, which could not be restored by heating.
關鍵字(中)	★ 拓樸絕緣體 ★ 半導體 ★ 表面改質 ★ 電子繞射 ★ 探針顯微 ★ 光電子能譜	關鍵字(英)	★ topological insulator ★ semiconductor ★ surface modification ★ electron diffraction ★ probe microscopy ★ photoelectron spectroscopy
論文目次	摘要 i Abstract ii 誌謝 iii 目錄 iv 圖目錄 vi 表目錄 ix 1. 簡介 1 2. 文獻回顧 3 2.1 Bi2Te3 製備方式 3 2.2 探討 Bi2Te3表面變化之文獻 5 2.3 Bi 雙層對拓樸絕緣體表面之影響 8 3. 儀器原理 21 3.1 低能量電子繞射儀 21 3.1.1 簡介 21 3.1.2 原理 21 3.1.3 Miller index 與 Wood’s notation 23 3.2 同步輻射光源 23 3.2.1 光源產生 24 3.2.2 光束聚焦 24 3.3 X 光光電子譜術 25 3.3.1 原理 25 3.3.2 化學位移 26 3.3.3 歐傑電子 27 3.3.4 費米能級 28 3.4 掃描穿隧顯微鏡 28 3.4.1 原理 28 3.4.2 STM 構造與操作 30 3.4.3 探針製作 31 3.5 角解析光電子能譜術 32 3.5.1 簡介 32 3.5.2 原理 32 3.6 超高真空系統 33 3.6.1 簡介 33 3.6.2 氣流(Gas Flow) 34 3.6.3 傳導率(Conductance) 35 3.6.4 捲渦式幫浦 35 3.6.5 分子渦輪幫浦 36 3.6.6 離子幫浦 36 3.6.7 鈦昇華幫浦 37 4. 結果與討論 51 4.1 LEED 結果與討論 51 4.2 XPS 結果與討論 51 4.2.1 在大氣環境中劈裂之樣品表面 52 4.2.2 受氧化樣品加熱後的表面檢測 57 4.2.3 在真空環境中劈裂之樣品表面 57 4.2.4 在 N2 及 O2環境中劈裂之樣品表面 58 4.3 STM 結果與討論 59 4.3.1 在真空環境中劈裂之樣品表面 59 4.3.2 在大氣環境中劈裂之樣品表面 60 4.4 ARPES 結果與討論 61 4.5 總結 Bi2Te3 表面變化過程 62 5. 結論 78 6. 參考資料 79 附錄 : 配合 Attenuation Model 的圖形使用者介面—Python程式碼 82
參考文獻	[1] 黃榮俊。「拓樸絕緣體之能帶結構、輸運性質與場效電晶體元件之介紹與研 究」。物理雙月刊，201710 (39:5 期)。 [2] Y. Zang, T. Jiang, Y. Gong, Z. Guan, C. Liu, M. Liao, K. Zhu, Z. Li, L. Wang, W. Li, C. Song, D. Zhang, Y. Xu, K. He, X. Ma, S. Zhang, and Q. Xue. Adv. Funct. Mater. 28, 1802723 (2018). [3] F. Zhu, W. Chen, Y. Xu, C. Gao, D. Guan, C. Liu, D. Qian, S. Zhang, and J. Jia. Nat. Mater. 14, 1020 (2015). [4] H. Liu, H. Yuan, N. Fukui, L. Zhang, J. Jia, Y. Iwasa, M. Chen, T. Hashizume, T. Sakurai, and Q. Xue. Cryst. Growth Des. 10, 4491–4493 (2010). [5] A. Netsou, D. Muzychenko, H. Dausy, T. Chen, F. Song, K. Schouteden, M. Bael, and C. Haesendonck. ACS Nano. 14, 13172–13179 (2020). [6] V. Atuchin, V. Golyashov, K. Kokh, I. Korolkov, A. Kozhukhov, V. Kruchinin, I. Loshkarev, L. Pokrovsky, I. Prosvirin, K. Romanyuk, and O. Tereshchenko. J. Solid State Chem. 236, 203-208 (2015). [7] Y. Li, G. Wang, X. Zhu, M. Liu, C. Ye, X. Chen, Y. Wang, K. He, L. Wang, X. Ma, H. Zhang, X. Dai, Z. Fang, X. Xie, Y. Liu, X. Qi, J. Jia, S. Zhang, and Q. Xue. Adv. Mater. 22, 4002–4007 (2010). [8] 葉唐喬。科技部補助大專學生研究計畫研究成果報告 (2021)。 [9] Y. Chen, J. Analytis, J. Chu, Z. Liu, S. Mo, X. Qi, H. Zhang, D. Lu, X. Dai, Z. Fang, S. Zhang, I. Fisher, Z. Hussain, and Z. Shen. Science. 325, 178-181 (2009). [10] D. Music, K. Chang, P. Schmidt, F. Braun, M. Heller, S. Hermsen, P. Pöllmann, T. Schulzendorff, and C. Wagner. J. Phys.: Condens. Matter 29, 485705 (2017). [11] H. Bando, K. Koizumi, Y. Oikawa, K. Daikohara, V. Kulbachinskii, and H. Ozaki J. Phys.: Condens. Matter 12, 5607–5616 (2000). [12] C. Thomas, M. Vallon, M. Frith, H. Sezen, S. Kushwaha, R. Cava, J. Schwartz, and S. Bernasek. Chem. Mater. 28, 35−39 (2016). [13] A. Netsou, U. Thupakula, J. Debehets, T. Chen, B. Hirsch, A. Volodin, Z. Li, F. Song, J. Seo, S. Feyter, K. Schouteden, and C. Haesendonck. Nanotechnology 28, 335706 (2017). [14] R. Macedo, S. Harrison, T. Dorofeeva, J. Harris, and R. Kiehl. Nano Lett. 15, 4241 (2015). [15] D. Kong, J. Cha, K. Lai, H. Peng, J. Analytis, S. Meister, Y. Chen, H. Zhang, I. Fisher, Z. Shen, and Y. Cui. ACS Nano. 5, 4698–4703 (2011). [16] Y. Chen, J. Chu, J. Analytis, Z. Liu, K. Igarashi, H. Kuo, X. Qi, S. Mo, R. Moore, D. Lu, M. Hasimoto, T. Sasagawa, S. Zhang, I. Fisher, Z. Hussain, and Z. Shen. Science. 329, 659– 662 (2010). [17] K. Zhang, D. Ding, C. Yang, Y. Gan, S. Li, W. Huang, Y. Song, Z. Jia, X. Li, Z. Zhu, J. Wen, M. Chen, and S. Li. Phys. Rev. B 93, 235445 (2016). [18] M. Chen, J. Peng, H. Zhang, L. Wang, K. He, X. Ma, and Q. Xue. Appl. Phys. Lett. 101, 081603 (2012). [19] H. Benia, C. Lin, K. Kern, and C. Ast. Phys. Rev. Lett. 107, 177602 (2011). [20] M. Kuznetsov, L. Yashina, J. Barriga, I. Ogorodnikov, A. Vorokh, A. Volykhov, R. Koch, V. Neudachina, M. Tamm, A. Sirotina, A. Varykhalov, G. Springholz, G. Bauer, J. Riley, and O. Rader. Phys. Rev. B 91, 085402 (2015). [21] A. Tamtögl, D. Campi, M. Bremholm, E. Hedegaard, B. Iversen, M. Bianchi, P. Hofmann, N. Marzari, G. Benedek, J. Ellis, and W. Allison. Nanoscale 10, 14627-14636 (2018). [22] S. Nakajima. J. Phys. Chem. Solids 24, 479–485 (1963). [23] H. Shinotsuka, S. Tanuma, C. Powell, and D. Penn. Surf. Interface Anal. 47, 871–888 (2015). [24] P. Hofmann. Progress in Surface Science 81, 191–245 (2006). [25] Hans Lüth. 2010. Solid Surfaces, Interfaces and Thin Films, Fifth Edition. Springer. [26] Ewald construction for electron diffraction on a two-dimensional lattice, side view. https://zh.m.wikipedia.org/zh-tw/File:Ewald_construction_for_electron_diffraction_on_a_twodimensional_lattice,_side_view.svg [27] 同步加速器光源簡介, 國家同步輻射研究中心網站。 https://www.nsrrc.org.tw/chinese/lightsource.aspx [28] TLS Beamline-24A1, 國家同步輻射研究中心網站。 https://tls.nsrrc.org.tw/bd_page.aspx?lang=en&port=24A1&pid=1386 [29] X 射線光電子能譜儀, 科學 Online -臺灣大學。 https://highscope.ch.ntu.edu.tw/wordpress/?tag=x%E5%B0%84%E7%B7%9A [30] Quantum tunnelling, Wikipedia, The Free Encyclopedia. https://en.wikipedia.org/wiki/Quantum_tunnelling [31] UHV SPM booklet. RHK Technology. https://www.rhk-tech.com/wp-content/uploads/2015/12/RHK-Beetle uhv.brochure.linear-edit.pdf [32] rportal.lib.ntnu.edu.tw. [33] RCAS-SPM 實驗室日誌。 https://rcas-spm.blogspot.com/2011/11/stm-tip.html [34] Andrea Damascelli. Phys. Scr. 109, 61-74 (2004). [35] Stefan Hüfner. 2003. Photoelectron Spectroscopy, Third Edition. Springer. [36] Varian. 1992. Basic Vacuum Practice, Third Edition. Varian Associates. [37] SRL 日立渦卷式空壓機產品介紹。 https://www.e-compressor.com.tw/product05.php
指導教授	陸大安(Dah-An Luh)	審核日期	2023-7-8
推文	facebook   plurk   twitter   funp   google   live   udn   HD   myshare   reddit   netvibes   friend   youpush   delicious   baidu
網路書籤	Google bookmarks   del.icio.us   hemidemi   myshare