Sublimation Point Depression of Small-Molecule Semiconductors by Sonocrystallization

NCU Institutional Repository > 工學院 > 化學工程與材料工程研究所 > 期刊論文 > Item 987654321/26436

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26436

題名:	Sublimation Point Depression of Small-Molecule Semiconductors by Sonocrystallization
作者:	Lee,T;Chang,SC
貢獻者:	化學工程與材料工程學系
關鍵詞:	FIELD-EFFECT TRANSISTORS;THIN-FILM TRANSISTORS;CRYSTAL-STRUCTURE;ORGANIC SEMICONDUCTORS;EVAPORATED PENTACENE;HIGH-PERFORMANCE;ALQ(3);CRYSTALLIZATION;POLYMORPHS;TRIS(8-HYDROXYQUINOLINE)ALUMINUM(III)
日期:	2009
上傳時間:	2010-06-29 17:28:01 (UTC+8)
出版者:	中央大學
摘要:	Small-molecule semiconductor solids such as pentacene and tris(8-hydroxyquinoline)aluminum(III) (Alq3) were dispersed in a poor solvent, like water, and insonated in a 10 mL scintillation vial with an output frequency of 20 kHz, a voltage of 1500 V, and an optimal induction time for 10 min at -13 degrees C. Sonocrystallization, at a low bulk solution temperature, gave pentacene powders of a high lattice energy difference value, Delta E-latt of 2.258 J/g (i.e., 0.6285 kcal/mol) caused by the poor crystallinity of 69% and produced Alq3 powders with only 37 wt % of the stable alpha-form and 63 wt % of the metastable epsilon-form mixed with an amorphous phase. Therefore, insonated pentacene and Alq3 powders had depressed sublimation points of 210 and 180 degrees C, respectively. However, surface energy and impurities had nothing to do with the sublimation point depression. The sublimation point depression of target materials could reduce the heating, and cooling duty of the vapor-phase deposition method for the manufacturing of organic light-emitting diodes (OLEDs), organic thin-film transistors (OTFTs), and photovoltaic (PV) cells drastically, because the total radiant-heat-transfer rate between heated surfaces is proportional to the fourth power of the absolute temperature according to the Stefan-Boltzmann law.