English  |  正體中文  |  简体中文  |  Items with full text/Total items : 65317/65317 (100%)
Visitors : 21372423      Online Users : 258
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/3844


    Title: 高韌性環氧樹脂底膠之開發;Developement of a high toughness primer
    Authors: 黃向義;Shiang-Yi Huang
    Contributors: 化學工程與材料工程研究所
    Keywords: 水下換能器;水氣滲透;環氧樹酯;增韌;底膠;Primer;Toughening;Epoxy Resin;Water-vapor Permeation;Sub-water Transformer
    Date: 2004-07-13
    Issue Date: 2009-09-21 12:24:04 (UTC+8)
    Publisher: 國立中央大學圖書館
    Abstract: 由於改進環氧樹脂易脆的缺點,前人摻入CTBN增韌效果為佳。而增韌的原因,過去Cavitation-shear yielding漸被證明並接受。增韌系統乃藉由膠粒與周圍環氧樹脂的cavitaion,並引發膠粒與膠粒間產生shear yielding。本論文乃為高韌性環氧樹脂底膠之開發,其目的乃用於水下換能器外圍,與PU底膠必須有一多功能性之防水底膠保護之。歷經環氧樹酯配方的收尋與判斷,液態橡膠的摻合與配方的建立,加工方式的改良,及其增韌後環氧樹酯性質之鑑定。目前已獲得一組可用之環氧樹酯配方;其拉伸強度為61.49至42.56 Mpa;拉伸剛性為2.13至1.61 Gpa;玻璃轉移溫度為90至60℃;破裂能量為1442至5132 J/ m2。 根據實驗結果所示,純環氧樹脂基材,隨著基材的變軟shear-yielding略增,破壞能量些微提高。但於純環氧樹脂基材內加入橡膠後,可使得韌性全面提升;且玻璃轉移溫度亦適用於使用溫度之上,並符合其水下換能器能有適當的延展性、加工性與低水氣滲透性。故以此增韌系統為其探討方向。
    Appears in Collections:[化學工程與材料工程研究所] 博碩士論文

    Files in This Item:

    File SizeFormat
    0KbUnknown644View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明