Discontinuous coarsening of discontinuous precipitates in a Co-6 at.% Mo alloy

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/39069

Title:	Discontinuous coarsening of discontinuous precipitates in a Co-6 at.% Mo alloy
Authors:	Lee,SL;Lee,KC;Chuang,TH
Contributors:	物理研究所
Keywords:	KINETICS;MORPHOLOGY;LAMELLAE;LAYER
Date:	1998
Issue Date:	2010-07-08 14:03:56 (UTC+8)
Publisher:	中央大學
Abstract:	The morphology and growth kinetics of the discontinuous coarsening of discontinuous precipitates in a Co-6 at.% Mo alloy have been investigated at temperatures ranging from 773 to 998 K by optical and scanning electron microscopy and X-ray diffraction. At all aging temperatures the alloy was observed to decompose completely by discontinuous precipitation into a fine lamellar structure of b.c.t. Co rich solid solution and an intermetallic compound phase of Co3Mo. This lamellar structure was then decomposed at all aging temperatures by a discontinuous coarsening reaction. This reaction occurred at a much slower rate than the primary discontinuous precipitation reaction and resulted in a much coarser lamellar structure of the same phases. Through the measurements of the growth rates and lamellar spacings for both the discontinuous precipitation and discontinuous coarsening reactions, the grain boundary diffusion coefficients (SdeltaDb) were analyzed using the kinetic model of Petermann and Hornbogen. By comparison with the diffusion data in literature, it was concluded that the reactions were controlled by grain boundary diffusion in the reaction fronts of the discontinuous precipitates. (C) 1998 Elsevier Science S.A. All rights reserved.
Relation:	MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
Appears in Collections:	[Graduate Institute of Physics] journal & Dissertation

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	488	View/Open

社群 sharing

Loading...