Discontinuous coarsening of discontinuous precipitates in a Co-6 at.% Mo alloy

NCU Institutional Repository > 理學院 > 物理研究所 > 期刊論文 > Item 987654321/39069

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/39069

题名:	Discontinuous coarsening of discontinuous precipitates in a Co-6 at.% Mo alloy
作者:	Lee,SL;Lee,KC;Chuang,TH
贡献者:	物理研究所
关键词:	KINETICS;MORPHOLOGY;LAMELLAE;LAYER
日期:	1998
上传时间:	2010-07-08 14:03:56 (UTC+8)
出版者:	中央大學
摘要:	The morphology and growth kinetics of the discontinuous coarsening of discontinuous precipitates in a Co-6 at.% Mo alloy have been investigated at temperatures ranging from 773 to 998 K by optical and scanning electron microscopy and X-ray diffraction. At all aging temperatures the alloy was observed to decompose completely by discontinuous precipitation into a fine lamellar structure of b.c.t. Co rich solid solution and an intermetallic compound phase of Co3Mo. This lamellar structure was then decomposed at all aging temperatures by a discontinuous coarsening reaction. This reaction occurred at a much slower rate than the primary discontinuous precipitation reaction and resulted in a much coarser lamellar structure of the same phases. Through the measurements of the growth rates and lamellar spacings for both the discontinuous precipitation and discontinuous coarsening reactions, the grain boundary diffusion coefficients (SdeltaDb) were analyzed using the kinetic model of Petermann and Hornbogen. By comparison with the diffusion data in literature, it was concluded that the reactions were controlled by grain boundary diffusion in the reaction fronts of the discontinuous precipitates. (C) 1998 Elsevier Science S.A. All rights reserved.
關聯:	MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING