Characterization of GaN epitaxial layers on SiC substrates with AlxGa1-xN buffer layers

NCU Institutional Repository > 理學院 > 物理研究所 > 期刊論文 > Item 987654321/39118

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/39118

題名:	Characterization of GaN epitaxial layers on SiC substrates with AlxGa1-xN buffer layers
作者:	Lin,CF;Cheng,HC;Feng,MS;Chi,GC
貢獻者:	物理研究所
關鍵詞:	VAPOR-PHASE EPITAXY;DEPENDENCE;GROWTH
日期:	1997
上傳時間:	2010-07-08 14:05:29 (UTC+8)
出版者:	中央大學
摘要:	High quality GaN epitaxial layers were obtained with AlxGa1-xN buffer layers on 6H-SiC substrates. The low-pressure metalorganic chemical vapor deposition (LP-MOCVD) method was used. The 500 Angstrom thick buffer layers of AlxGa1-xN (0 less than or equal to x less than or equal to 1) were deposited on SiC substrates at 1025 degrees C. The FWHM of GaN (0004) X-ray curves are 2-3 arcmin, which vary with the Al content in AlxGa1-xN buffer layers. An optimum Al content is found to be 0.18. The best GaN epitaxial film has the mobility and carrier concentration about 564 cm(2) V-1 s(-1) and 1.6 x 10(17) cm(-3) at 300 K. The splitting diffraction angle between GaN and AlxGa1-xN were also analyzed from X-ray diffraction curves. (C) 1997 Elsevier Science S.A.
關聯:	MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY
顯示於類別:	[物理研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	383	檢視/開啟

在NCUIR中所有的資料項目都受到原著作權保護.

社群 sharing