    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/50022


    Title: Preparation of Highly Adhesive and Superhydrophobic Epoxy-Based Thin Film by Sol-Gel Process
    Authors: Wu,GY;Wang,SS;Wu,JC;Hsu,MY;Chen,H
    Contributors: 材料科學與工程研究所
    Keywords: SUPER-HYDROPHOBIC FILMS;SILICA-BASED SURFACES;WATER-REPELLENT;FABRICATION;TETRAETHOXYSILANE;POLYPROPYLENE;PRECURSORS;GLYCOL
    Date: 2011
    Issue Date: 2012-03-27 16:29:14 (UTC+8)
    Publisher: 國立中央大學
    Abstract: In this study the preparation of a superhydrophobic epoxy-based thin film with excellent high adhesion properties was carried out by mixing epoxy polymer solution, MTMOS solution, and silica powder. It was found that the adhesion between the film and a substrate could be improved by adding PET fibers to the above solution. The characteristic properties of the as-prepared films were analyzed by contact angle measurements, scanning electron microscopy (SEM) and by atomic force microscopy (AFM). The adhesion between the film and the substrate was estimated by the cross-cut method. The experimental parameters were: the mole fraction of MTMOS, weight fraction of silica powder, weight fraction of PET fibers, and the curing temperature. The result indicated that the contact angle and the sliding angle of the hybrid film were 153 degrees and 4 degrees, respectively, and the adhesion test result was very good (5B degree), while the mole fraction of MTMOS was 0.4, the silica powder concentration was 30 wt%, and the PET fibers concentration was 0.15 wt%, with the curing temperature in the range of 130-180 degrees C. (C) Koninklijke Brill NV, Leiden, 2011
    Relation: JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY
    Appears in Collections:[材料科學與工程研究所 ] 期刊論文

    Files in This Item:

    File Description SizeFormat
    index.html0KbHTML526View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明