La(0.6)Sr(0.4)Co(0.2)Fe(0.8)O(3) protective coatings for solid oxide fuel cell interconnect deposited by screen printing

NCUIR > Engineering College > Departmant of Mechanical Engineering > journal & Dissertation > Item 987654321/50109

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/50109

Title:	La(0.6)Sr(0.4)Co(0.2)Fe(0.8)O(3) protective coatings for solid oxide fuel cell interconnect deposited by screen printing
Authors:	Tsai,MJ;Chu,CL;Lee,S
Contributors:	機械工程學系
Date:	2010
Issue Date:	2012-03-27 17:03:40 (UTC+8)
Publisher:	國立中央大學
Abstract:	La(0.6)Sr(0.4)Co(0.2)Fe(0.8)O(3) (LSCF) is applied on a Crofer22 APU interconnect for solid oxide fuel cells (SOFCs) by screen-printing method. The above coated alloy was first checked for their compositions, morphology and interface conditions. It was then tested in a simulated oxidizing environment, 800 degrees C for 200 h. The results showed that the LSCF film can change the oxidation behavior of Crofer22 APU. After sintering the screen printed alloy was under 1050 degrees C in N(2) atmosphere, the adhesion between the LSCF layer and alloy substrate is excellent. Long-term electrical resistance measurement indicated that area-specific resistance (ASR) of the alloy with coated film is significantly lower than that of the uncoated. The use of LSCF coating for metallic interconnect could reduce working temperature for solid oxide fuel cell. Published by Elsevier B.V.
Relation:	JOURNAL OF ALLOYS AND COMPOUNDS
Appears in Collections:	[Departmant of Mechanical Engineering ] journal & Dissertation

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	401	View/Open

社群 sharing