La(0.6)Sr(0.4)Co(0.2)Fe(0.8)O(3) protective coatings for solid oxide fuel cell interconnect deposited by screen printing

NCU Institutional Repository > 工學院 > 機械工程學系 > 期刊論文 > Item 987654321/50109

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/50109

题名:	La(0.6)Sr(0.4)Co(0.2)Fe(0.8)O(3) protective coatings for solid oxide fuel cell interconnect deposited by screen printing
作者:	Tsai,MJ;Chu,CL;Lee,S
贡献者:	機械工程學系
日期:	2010
上传时间:	2012-03-27 17:03:40 (UTC+8)
出版者:	國立中央大學
摘要:	La(0.6)Sr(0.4)Co(0.2)Fe(0.8)O(3) (LSCF) is applied on a Crofer22 APU interconnect for solid oxide fuel cells (SOFCs) by screen-printing method. The above coated alloy was first checked for their compositions, morphology and interface conditions. It was then tested in a simulated oxidizing environment, 800 degrees C for 200 h. The results showed that the LSCF film can change the oxidation behavior of Crofer22 APU. After sintering the screen printed alloy was under 1050 degrees C in N(2) atmosphere, the adhesion between the LSCF layer and alloy substrate is excellent. Long-term electrical resistance measurement indicated that area-specific resistance (ASR) of the alloy with coated film is significantly lower than that of the uncoated. The use of LSCF coating for metallic interconnect could reduce working temperature for solid oxide fuel cell. Published by Elsevier B.V.
關聯:	JOURNAL OF ALLOYS AND COMPOUNDS
显示于类别:	[機械工程學系] 期刊論文