應用於高溫氣體過濾之氧化鋯奈米纖維濾網

NCU Institutional Repository > 工學院 > 化學工程與材料工程研究所 > 博碩士論文 > Item 987654321/74044

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/74044

題名:	應用於高溫氣體過濾之氧化鋯奈米纖維濾網
作者:	李政憲;Li, Zheng-Xian
貢獻者:	化學工程與材料工程學系
關鍵詞:	氧化鋯;靜電紡絲;奈米纖維
日期:	2017-08-23
上傳時間:	2017-10-27 13:00:29 (UTC+8)
出版者:	國立中央大學
摘要:	本研究主要利用電紡絲技術製備具有可撓性之氧化鋯奈米纖維網並應用於高溫氣體之過濾。我們使用之起始物為表面醋酸改質之氧化鋯奈米粒子(ZA)所形成透明水性溶膠。並藉由醋酸與水之添加調整溶液之導電度與表面張力，透過ZA與聚乙烯吡咯烷酮(PVP)濃度調整溶液黏度，同時將無機物與有機物之體積比控制在30/70以上。在適當之極化電場及溶液流速下可製備出平滑沒有珠狀結構的連續纖維。經過乾燥後只要以500°C鍛燒就可將有機物移除。因為不產生大幅度晶相轉變與燒結，所以氧化鋯纖維膜保有其可撓性並且可承受400次以上180°彎折。但是由於我們未添加氧化釔，所以在800°C高溫鍛燒後會有晶相轉變及體積收縮而變脆弱。經過不同鍛燒溫度下測試，確定可撓性與XRD晶相變化有直接關係。最後我們透過電紡參數的調整製備出不同直徑之奈米纖維且厚度適當之可撓性濾材，進行氯化鈉粉塵之過濾測試，找出過濾效率最高而壓損較低的適當濾材製備方法。;Electrospinning is a scalable process for the preparation of flexible zirconia nanofibrous web useful as a hot gas filter. Composite fibers are formed under polarized electric field from a solution containing zirconium salt and a hydrophilic polymer (PVP) and are later transformed into zirconia via calcination. In this study, the precursor employed was a transparent aqueous sol of zirconia nanocrystals modified with acetate ligand. The surface tension and the conductivity of the precursor were adjusted by the addition of acetic acid and water. The viscosity and the inorganic/organic ratio were adjusted by the concentration of ZA and PVP. Under proper operation conditions, smooth fibrous web without bead structure could be electrospun. The zirconia mat obtained remained flexibility after calcination at 500°C and withstood 400 times of 180° bending. This temperature is lower than that required by literature processes using amorphous precursor. Consequently, the problem of fiber fracture due to crystallization was eliminated. Upon increasing the calcination temperature and duration, the monoclinic phase started to appear which break the fiber and remove its flexibility due to volume expansion. We further prepared flexible mats with nanofibers of different diameters, and study the filtration of NaCl dust. Our mat could achieve more than 99.9% removal with less than 200 Pa pressure drop at 20 LPM flow rate.
顯示於類別:	[化學工程與材料工程研究所] 博碩士論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	361	檢視/開啟

在NCUIR中所有的資料項目都受到原著作權保護.

社群 sharing

資料載入中.....