Dynamic strain aging and grain size reduction effects on the fatigue resistance of SA533B3 steels

NCUIR > Engineering College > Graduate Institute of Mechanical Engineering > journal & Dissertation > Item 987654321/30841

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/30841

Title:	Dynamic strain aging and grain size reduction effects on the fatigue resistance of SA533B3 steels
Authors:	Huang,JY;Hwang,JR;Yeh,JJ;Chen,CY;Kuo,RC;Huang,JG
Contributors:	機械工程研究所
Keywords:	PRESSURE-VESSEL STEELS;LOW-CYCLE FATIGUE;LOW-CARBON STEEL;GROWTH RATE PROPERTIES;MICROSTRUCTURAL EVALUATION;CRACK TIP;TEMPERATURE;DAMAGE;BEHAVIOR;ENVIRONMENTS
Date:	2004
Issue Date:	2010-07-06 16:28:34 (UTC+8)
Publisher:	中央大學
Abstract:	Constant amplitude axial fatigue tests were conducted on SA533B3 steels with four levels of sulfur content at room temperature and 300 degreesC. Fatigue life was significantly affected by the inclusions. Fractographic examination results suggested that in
Relation:	JOURNAL OF NUCLEAR MATERIALS
Appears in Collections:	[Graduate Institute of Mechanical Engineering] journal & Dissertation