Dynamic strain aging and grain size reduction effects on the fatigue resistance of SA533B3 steels

NCU Institutional Repository > 工學院 > 機械工程研究所 > 期刊論文 > Item 987654321/30841

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/30841

题名:	Dynamic strain aging and grain size reduction effects on the fatigue resistance of SA533B3 steels
作者:	Huang,JY;Hwang,JR;Yeh,JJ;Chen,CY;Kuo,RC;Huang,JG
贡献者:	機械工程研究所
关键词:	PRESSURE-VESSEL STEELS;LOW-CYCLE FATIGUE;LOW-CARBON STEEL;GROWTH RATE PROPERTIES;MICROSTRUCTURAL EVALUATION;CRACK TIP;TEMPERATURE;DAMAGE;BEHAVIOR;ENVIRONMENTS
日期:	2004
上传时间:	2010-07-06 16:28:34 (UTC+8)
出版者:	中央大學
摘要:	Constant amplitude axial fatigue tests were conducted on SA533B3 steels with four levels of sulfur content at room temperature and 300 degreesC. Fatigue life was significantly affected by the inclusions. Fractographic examination results suggested that in
關聯:	JOURNAL OF NUCLEAR MATERIALS
显示于类别:	[機械工程研究所] 期刊論文