Epitaxy and characterization of III-nitride high electron mobility transistors on silicon for RF applications

NCU Institutional Repository > 資訊電機學院 > 電機工程研究所 > 博碩士論文 > Item 987654321/85116

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/85116

題名:	Epitaxy and characterization of III-nitride high electron mobility transistors on silicon for RF applications
作者:	辛耶兒;Sanyal, Indraneel
貢獻者:	電機工程學系
關鍵詞:	GaN;HEMT;GaN on Silicon;RF HEMT;AlInGaN
日期:	2021-01-28
上傳時間:	2021-03-18 17:42:30 (UTC+8)
出版者:	國立中央大學
摘要:	在高功率和高頻應用中，逐漸地要使用基於GaN的高電子遷移率電晶體（HEMT）。電子傳輸特性在RF和功率開關性能中起著重要作用。而高的電子遷移率能減少電子從汲極到源極的傳輸時間且高電子密度可提高跨導和電流密度。因此，就磊晶而言，在設計新型電晶體中電子傳輸特性的好壞是非常重要的。另外AlGaN/GaN異質結構通常在2100 cm2 / Vs以上顯示出電子遷移率，但在含銦的異質結構中卻沒有那麼明顯。GaN通道，異質界面和勢壘均值電子散射。因此，克服含銦異質結構中有限的傳輸性能是很重要的。此外，AlGaN / GaN異質結構可能是研究異質界面的出色工具。因此，首先通過在不同的生長條件下調製本質氮化鎵的表面缺陷，例如在氮氣或氫氣下磊晶氮化鎵或使用不同Ga的前驅物，來控制限制在AlGaN / GaN量子阱中的影響2DEG散射的異質界面特性。而在磊晶不同的Ga前驅物的試片中從二次離子質譜（SIMS）深度曲線表明，通過在厚的GaN緩衝層末端將載氣從H2更改為N2，可將殘留碳濃度從4x1017 cm-3降低到?2x1017 cm-3。TEG的使用進一步降低了GaN通道中的殘留碳濃度，變為6.4x1016 cm-3。在樣品中GaN通道分別在H2環境中與TMG和TEG。一起生長的情況下，在10K下的遷移率分別達到7900 cm2 / Vs和9360 cm2 / Vs。更進一步將載氣從H2轉化為N2，在帶有TEG生長的GaN通道的樣品中，遷移率達到28000。 cm2 /Vs。但是，與在氮氣相環境中磊晶的樣品中發現2DEG下降了46％，是因為AlGaN勢壘中的Al含量降低。對散射機制研究表明，三個樣品中霍爾遷移率的一部分介於9.2x103 cm2 / Vs至3.4x104 cm2 / Vs之間，有未知的散射機制控制。不能通過考慮所有常規的散射機制（如聲子-聲子散射，界面堆疊散射，位錯深入分析表明，GaN/AlN/AlGaN的界面帶電會嚴重影響取向電子的散射。與在H2環境中使用TMG生長的GaN溝道相比，在H2和N2環境中使用TEG生長GaN氮化鎵通道/界面時，從與溫度相關的霍爾遷移率中提取的界面特性表示，帶電狀態降低了29％和80％。從而，在製造的高電子遷移速率電晶體上進行的與溫度有關的次臨界斜率中估計界面狀態與從與溫度有關的霍爾測量中擷取的帶電介面狀態非常吻合，因此進一步支持了這一假設。這也提供了通過III族氮充分了解GaN異質結構中的這種新散射機制，可能導致將來設計高效的III型氮化物器件。 AlInN位障層的主要問題是由於不互融性所導致。這導致位障層內部銦的不均勻，並導致電性能下降。與AlInN相比，AlGaN是最穩定的合金。因此，這兩種合金的組合可以提高四元AlInGaN合金的熱力學穩定性。通過向AlInN合金中添加少量Ga，AlInGaN / GaN異質結構的幾位作者已經報告了電子遷移率的顯著改善。然而高電子遷移率電晶體的四元化合物得位障層設計和磊晶可能很困難。因為與晶格匹配的AlInN相比，文獻中關於材料的成分尚無共識。這種複雜合金的設計也沒有指導方針。我們提出了一種新的機制，其中熱力學穩定性在控制這些異質結構中的電子傳輸性質中起著重要作用。對於各種成分（0.5?Al?0.8，In = 0.2，0.15，0.1），已經對AlInGaN勢壘的熱力學穩定性進行了定量研究當Ga原子僅取代Al原子時，觀察到熱力學穩定性也緩慢變化。當同時Al0.83In0.17N層中將銦原子替換已經發現，由於位障層中總彈性應力的顯著降低，Al含量在65％至70％範圍內且摻入含量為10％時，可以觀察到熱力學穩定性的顯著改善。例如，如本文中的實驗觀察所證明的，其導致的最高電子遷移率，即電子遷移率2,090 cm2 / Vs，片載流子密度。為1.09×1013 cm-2。因此，除了通常觀察到的散射機制之外，熱力學穩定性至少可以部分地保持為AlInGaN / GaN異質結構中電子遷移率的持續改善的原因。由這些AlInGaN / AlN / GaN異質結構製成的高電子遷移率半導體，生長在150 mm p型低電阻率（電阻率?20-100Ω-cm）矽基板上，展示了最新的Johnson的圖形。功績（JFOM）。三端崩潰擊穿電壓分別為69 V和127 V，電流增益終止頻率（fT）為83 GHz和63 GHz，功率增益頻率（fmax）為95 GHz和77 GHz，因為在閘極寬度長度為0.16μm並且閘極到汲極至距離距離分別為2μm和4μm的元件上實現了5.7 THz-V和8.1 THz-V如此高的JFOM。分析表明，較高的JFOM可能是由於在N2環境下使用TEG生長的GaN通道，使通道具有優異的電子傳輸性能和較低的殘留碳濃度。 2D元件仿模擬進一步表明，GaN通道中的陷阱密度應處於1016 cm-3的較低級，以避免寄生電荷對fT的影響。對於具有相似柵極長度的器件，fT和J-FOM與在高電阻率矽和SiC基板上獲得的報告值相當或更好。從而，由於強的TCAD大信號輸出功率模擬表明，即使存在寄生摻雜和導電矽基板，也可以通過最大程度地減少GaN摻雜中的缺陷和自由微小的載流子來顯著提高輸出功率。我們進一步提出了一種改進的等效電路模型，以考慮GaN和AlGaN摻雜的電導率。因此，此研究為在電晶體的低電阻矽基板上實現毫米波GaN HEMT提供了新的觀點。 ;The use of GaN-based high electron mobility transistors (HEMTs) is inevitable in high power and high-frequency applications. Electron transport properties play a significant role in determining the RF and power switching performances. High electron mobility reduces the electron transit time between the drain and the source. Whereas, high electron density improves the transconductance and current density. Therefore, in terms of epitaxy, electron transport properties are paramount in designing state-of-the-art transistors. Although, AlGaN barrier heterostructure routinely exhibits electron mobility above 2100 cm2/V-s, the same is not so obvious in the indium containing heterostructures. The GaN channel, the heterointerface and the barrier, all contribute to electron scattering. Therefore, it is important to address each one of these to overcome the limited transport properties in indium containing heterostructures. Furthermore, the scattering mechanisms in indium containing thin barrier heterostructures could be complex. Whereas, AlGaN/GaN heterostructures may be an excellent tool to study the heterointerface. Therefore, the heterointerface characteristics that influence the scattering of 2DEG, confined in the AlGaN/GaN quantum well, are first controlled by modulating the surface reconstruction of the intrinsic GaN channel under different in-situ growth conditions such as growing the GaN channel under either nitrogen or hydrogen ambient and with different Ga precursors such as trimethylgallium (TMG) and triethylgallium (TEG). The secondary ion mass spectroscopy (SIMS) depth profiles indicate that, by changing the carrier gas from H2 to N2 at the end of the thick GaN buffer, reduces the residual carbon concentration from 4x1017 cm-3 to ~2x1017 cm-3. The use of TEG resulted in further reduction of residual carbon concentration in the GaN channel down to 6.4x1016 cm-3. The mobility at 10K reaches up to 7900 cm2/V-s and 9360 cm2/V-s in samples where the GaN channel is grown with TMG and TEG respectively, both in H2 ambient. Further changing the carrier gas from H2 to N2, the mobility reaches up to 28000 cm2/V-s in the sample with TEG grown GaN channel. However, a 46% drop in 2DEG is also observed as compared to the samples grown in H2 ambient due to lower Al content in the AlGaN barrier. A systematic study of the scattering events reveals that a component of the Hall mobility, which ranges between 9.2x103 cm2/V-s to 3.4x104 cm2/V-s among the three samples is governed by unknown scattering events. This cannot be explained completely by considering all the conventional scattering mechanisms such as phonon-phonon scattering, interface roughness scattering, dislocation density scattering etc. An in-depth analysis reveals a significant scattering of channel electrons by the charged states at the GaN/AlN/AlGaN interface. The extracted interface states from the temperature-dependent Hall mobility indicates 29% and 80% reduction in charged states when the GaN channel/interface is grown using TEG in H2 and N2 ambient respectively as compared to the GaN channel grown with TMG in H2 ambient. Furthermore, the estimated interface states from the temperature-dependent subthreshold slops conducted on the fabricated high electron mobility transistors are in good agreement with the charged interface states extracted from the temperature-dependent Hall measurements and therefore, further supports the postulate. This also provides experimental evidence of electron scattering by the charged interface states in III-nitride heterostructures. A good understanding of this new scattering mechanism in GaN heterostructure may help in designing high-performance III-nitride devices in the future. The main problem with the AlInN barrier is indium segregation due to the highest immiscibility. This results in compositional inhomogeneity within the barrier and often responsible for electrical performance degradation. It is known that AlGaN is the most stable alloy as compared to AlInN. Therefore, a combination of these two alloys may increase the thermodynamic stability in the quaternary AlInGaN alloy. Significant improvement in electron mobility has been reported by several authors in AlInGaN/GaN heterostructures by adding small amount of Ga to the AlInN alloy. However, design and epitaxy of a quaternary barrier for the high electron mobility transistors can be difficult. Moreover, there is no agreement on the composition of the material in the literature as opposed to the lattice-matched AlInN. There was no guideline as well on the design of this complex alloy. We propose a new mechanism where thermodynamic stability plays an important role in controlling the electron transport properties in these heterostructures. A quantitative investigation of the thermodynamic stability of AlInGaN barrier has been carried out analytically, for a wide range of compositions (0.5 ? Al ? 0.8, In = 0.2, 0.15, 0.1). A slow change in the thermodynamic stability is observed when the Ga atoms replace only the Al atoms. In contrast, a significant improvement in thermodynamic stability is observed, when the indium atoms are replaced by the Ga atoms in the same Al0.83In0.17N layer. It is found that Al content in the range of 65% to 70% with 10% indium exhibit the highest thermodynamic stability within the calculated composition range owing to the significant reduction in total elastic strain in the barrier. Thereby, it leads to the highest electron mobility, as evidenced by the experimental observations in this work, i.e. electron mobility of 2,090 cm2/V-s with a sheet carrier density of 1.09x1013 cm-2. Therefore, the thermodynamic stability apart from commonly observed scattering mechanisms may at least be partially held responsible for the consistent improvement in electron mobility in AlInGaN/GaN heterostructures. The fabricated high electron mobility transistors out of these AlInGaN/AlN/GaN heterostructures, grown on 150 mm p-type low resistivity (resistivity~ 20-100 ?-cm) silicon substrate demonstrate state-of-the-art Johnson’s figure-of-merit (JFOM). Current gain cut-off frequency (fT) of 83 GHz and 63 GHz and power gain cut-off frequency (fmax) of 95 GHz and 77 GHz with a three-terminal off-state breakdown voltage of 69 V and 127 V, resulting in a high JFOM of 5.7 THz-V and 8.1 THz-V are achieved on the devices with a gate length of 0.16 m and gate to drain distance of 2 m and 4 m, respectively. The analysis suggests that the high JFOM could be due to the superior electron transport properties and lower residual carbon concentration in the channel due to the use of TEG grown GaN channel in N2 ambient. 2D device simulation further shows that the trap density in the GaN channel should be in the lower order of 1016 cm-3 to avoid the effect of parasitic charge modulation on fT. The fT and J-FOM are comparable or better than the reported values obtained on high resistivity silicon and SiC substrates for devices with similar gate length. On the other hand, the GaN-on-Si HEMTs on the LR-Si substrate exhibit lower power gain and power-added efficiency due to strong capacitive coupling effects. TCAD large signal output power simulation indicates significant improvements in output power by minimizing the defects and free charge carriers in the GaN buffer even in the presence of the parasitic channel conduction and the conductive silicon substrate. We further propose a modified equivalent circuit model of the parasitic conduction to take into account the conductivity of the GaN and AlGaN buffer. Therefore, this study shows a new viewpoint on realizing mm-wave GaN HEMTs on low resistivity silicon substrate for next-generation transistors.
顯示於類別:	[電機工程研究所] 博碩士論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	131	檢視/開啟

在NCUIR中所有的資料項目都受到原著作權保護.

社群 sharing

資料載入中.....