Refinement of the primary Si particles in hypereutectic aluminum alloy

NCUIR > Engineering College > Departmant of Mechanical Engineering > journal & Dissertation > Item 987654321/109033

Please use this identifier to cite or link to this item: https://ir.lib.ncu.edu.tw/handle/987654321/109033

Title:	Refinement of the primary Si particles in hypereutectic aluminum alloy
Authors:	李雄;Hsu, Chang-Chuan;Wang, Jian-Yih;Huang, Jian-Jia;Lee, Shyong
Contributors:	工學院機械工程學系
Keywords:	Aluminum base alloys;Automotive engineering;Characterization and Evaluation of Materials;Chemistry and Materials Science;Coarsening;Engineering Thermodynamics;Heat and Mass Transfer;Intermetallic compounds;Machines;Magnetic Materials;Magnetism;Manufacturing;Materials Science;Metallic Materials;Plastic deformation;Processes;Reduction;Silicon;Solid Mechanics;Thermal expansion;Weight reduction;재료공학
Date:	2012-08-01
Issue Date:	2026-04-23 15:25:26 (UTC+8)
Publisher:	Korean Institute of Metals and Materials;Springer: The Korean Institute of Metals and Materials
Abstract:	摘要： Al-Si alloys, with such excellent properties as low weight, low thermal expansion coefficient, and high wear-resistance, are ideal materials for the automobile and aerospace industries. However, their applications have been hampered by the coarsening of the primary-Si particles in Al-Si alloys. In this study, simple plastic deformation was used to reduce primary-Si particles and to improve the wear-resistance and mechanical strength of Al-Si alloys. Experimental results showed that mechanical rolling decreased the grain size of primary-Si particles in Al-Si alloys and reduced the variation in silicon particle size. After 60%-roll-reduction, the alloy showed an improved tensile strength of 340 MPa, which is attributed to the work hardening of the aluminum matrix and the dispersion strengthening of the primary-Si particles. Data from wear-resistance testing showed that rolling led to a reduction in wear loss. This improvement in wear resistance is due to the particle size refinement of silicon at a high percentage-roll-reduction. 其他題名： Met. Mater. Int 出版者： Springer: The Korean Institute of Metals and Materials 出版日期： 2012-08 出處： Metals and Materials International, 2012, 18(4), , pp.567-571 版權： The Korean Institute of Metals and Materials and Springer Netherlands 2012 識別號： ISSN: 1598-9623 識別號： EISSN: 2005-4149 識別號： DOI: 10.1007/s12540-012-4003-1
Appears in Collections:	[Departmant of Mechanical Engineering ] journal & Dissertation