    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/28204

    Title: Thermal reliability and characterization of InGaP Schottky contact with Ti/Pt/Au metals
    Authors: Lee,CT;Shiao,HP;Yeh,NT;Tsai,CD;Lyu,YT;Tu,YK
    Contributors: 光電科學研究所
    Keywords: EPITAXY
    Date: 1997
    Issue Date: 2010-06-29 19:43:49 (UTC+8)
    Publisher: 中央大學
    Abstract: We present the characteristics of Ti/Pt/Au Schottky contacts on wide bandgap InGaP semiconductors with surface pre-treatment before Schottky contact deposition, and investigate the influence of post heat treatment on Schottky diodes. With the pre-deposition surface etching by dilute HCl, dilute NH4OH, or buffer oxide etchant (BOE), the performance of Schottky diodes compared with samples without surface pre-treatment is improved significantly. Auger electron spectroscopy (AES) analysis of the thermally annealed Schottky diode has been performed to investigate the failure mechanism. No significant change was found for samples annealed up to 450 degrees C. However, a drastic degradation of the barrier height and the ideality factor was observed in samples annealed at 500 degrees C, which may be caused by the interdiffusion and penetration of metals into the semiconductor. Copyright (C) 1996 Elsevier Science Ltd
    Appears in Collections:[光電科學研究所] 期刊論文

    Files in This Item:

    File Description SizeFormat

    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明