退火Ge薄膜的性能研究;Research on the properties of the annealed Ge thin films

NCU Institutional Repository > 理學院 > 光電科學研究所 > 博碩士論文 > Item 987654321/82785

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/82785

題名:	退火Ge薄膜的性能研究;Research on the properties of the annealed Ge thin films
作者:	陳妙美;My, Tran Dieu
貢獻者:	光電科學與工程學系
關鍵詞:	虛擬鍺基板;III-V族太陽能電池;射頻磁控濺射;迴圈熱退火;Virtual Germanium Substrate;III-V solar cell;RF Magnetron Sputtering;Cycle Thermal annealing
日期:	2020-01-17
上傳時間:	2020-06-05 17:12:33 (UTC+8)
出版者:	國立中央大學
摘要:	由於高效率III-V族太陽能電池的性能優越，近來受到廣泛注意。而晶格匹配的基板在太陽能電池製造中被認為是非常重要的。本研究在Si基板上成長Ge磊晶薄膜，作為製造高效率III-V族太陽能電池的虛擬鍺基板。我們使用的兩種主要方法是射頻磁控濺射和迴圈熱退火。在Si基板上利用射頻磁控濺射沉積鍺磊晶薄膜與其它技術相比具有成本低的優點，也是一種安全的製造方法。為了降低螺紋狀差排密度（TDD）和減少缺陷，在Si表面沉積Ge磊晶薄膜後進行迴圈熱退火。由於Si和Ge在熱膨脹係數上的不匹配，退火後Ge薄膜的平面應力由壓縮變為拉伸。然後，我們將利用X光繞射（XRD）、拉曼光譜、原子力顯微鏡（AFM）和掃描電子顯微鏡（SEM）分析迴圈退火的影響以及TDD的還原機制。;III-V solar cells are becoming more widely known for their high efficiency and performance. Hence, a lattice - matched substrate is considered very important in their manufacturing. In this thesis, Ge epitaxial films on Si substrates are used as a virtual Ge substrate to manufacture highly efficient III-V solar cells. The two main methods employed are RF magnetron sputtering and cyclic thermal annealing. Ge epitaxial film will be deposited on the Si substrate via the RF magnetron sputtering method due to its lower cost and safety. Cycle thermal annealing is carried out after the deposition of Ge film on Si with the aim of reducing the threading dislocation density (TDD) and defects. Due to the mismatch between Si and Ge in terms of the thermal expansion coefficient, after the annealing process, the plane strain of the Ge film will be changed from compression to tension. We analyzed the effects of the cycle annealing as well as the TDD reduction mechanism via X-ray diffraction (XRD), Raman spectroscopy, atomic force microscopy (AFM), and scanning electron microscopy (SEM).