    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/50109

    Title: La(0.6)Sr(0.4)Co(0.2)Fe(0.8)O(3) protective coatings for solid oxide fuel cell interconnect deposited by screen printing
    Authors: Tsai,MJ;Chu,CL;Lee,S
    Contributors: 機械工程學系
    Date: 2010
    Issue Date: 2012-03-27 17:03:40 (UTC+8)
    Publisher: 國立中央大學
    Abstract: La(0.6)Sr(0.4)Co(0.2)Fe(0.8)O(3) (LSCF) is applied on a Crofer22 APU interconnect for solid oxide fuel cells (SOFCs) by screen-printing method. The above coated alloy was first checked for their compositions, morphology and interface conditions. It was then tested in a simulated oxidizing environment, 800 degrees C for 200 h. The results showed that the LSCF film can change the oxidation behavior of Crofer22 APU. After sintering the screen printed alloy was under 1050 degrees C in N(2) atmosphere, the adhesion between the LSCF layer and alloy substrate is excellent. Long-term electrical resistance measurement indicated that area-specific resistance (ASR) of the alloy with coated film is significantly lower than that of the uncoated. The use of LSCF coating for metallic interconnect could reduce working temperature for solid oxide fuel cell. Published by Elsevier B.V.
    Appears in Collections:[機械工程學系] 期刊論文

    Files in This Item:

    File Description SizeFormat

    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明